SUS631 Stainless Steel Coil 3/4H Condition Cold Rolled Steel Strip
Material SUS631, 17-7PH is a precipitationhardening stainless steel
that provides high strength and hardness,
excellent fatigue properties, good corrosion resistance, good
formability, and minimum distortion upon heat treatment.
Stainless SUS631 provides valuable property combinations
particularly well suited for aerospace applications.
Material SUS631 stainless also provides benefits for other
applications requiring high strength and
good corrosion resistance, as well as excellent properties for flat
springs at temperatures up to 600°F (316°C).
Material SUS631 requires three essential steps in heat treating:
1) Austenite conditioning.
2) Cooling to transform the austenite
2) to martensite.
3) Precipitation hardening to
2) Condition TH 1050 or RH 950.
To obtain the highest mechanical properties from the alloy,
Condition A material is transformed to martensite at the mill by
cold reduction to Condition C.
Hardening to Condition CH 900 is accomplished with a single,
low-temperature heat treatment.
Chemical composition % weight
|0.2% YS, Mpa||276||1276||1517||1310||1793|
|Elongation % in 2''||35||9||6||5||2|
AMS 5528 Sheet, Strip and Plate
AMS 5529 Sheet and Strip–Cold Rolled
MIL-S-25043 Plate, Sheet and Strip
ASTM A 693 Plate, Sheet and Strip
(Listed as Grade 631-UNS S17700)